Hardeners 1053S to 1059S Structural lamination epoxy system New hardeners salicylic acid free - Adjustable pot life from 10min to 14hours - Room temperature cure & mould release - TG up to 75°C - Excellent wetting properties on all reinforcements - For small to XXL size parts productions Datasheet V5 06.01.2021 - / Previous version - 27.05.2019

Abrir o catálogo na página 1

INTRODUCTION The 1050 epoxy laminating system is formulated to manufacture high performance lightweight structures with glass, carbon, aramid and basalt reinforcements with or without post-curing. This latest generation system, without CMR substances (including salicylic acid) according to GHS criteria is optimized with a low exotherm, low viscosity and excellent air release properties. This epoxy system is also suitable for the manufacture of small to very large structures and composite parts by wet lay-up, infusion, injection moulding or filament winding while guaranteeing low toxicity...

Abrir o catálogo na página 2

PHYSICAL CHARACTERISTICS Visual aspect Opalescent neutral liquid Transparent to yellow liquid Neutral to transparent yellow liquid Density at 23°C Mixed density at 23°C ISO 1675, ± 0.05 tolerance Mixed viscosity at 23°C (mPa.s) ISO 12058.2, ± 15% tolerance REACTIVITIES All hardeners mix with a 100/35 ratio and can be pre-blended together to precisely adjust the desired pot life. Systems Time at exothermic peak on 70 mL at 23°C Temperature at exothermic peak on 70mL at 23°C Gel time on 1mm thick film at 23°C *measurements realized on Trombotech® ** measurements realized on rheometer *NR :...

Abrir o catálogo na página 3

CURING AND POST-CURING In order to obtain the maximum thermo-mechanical properties, it is necessary to respect the recommended curing cycle. The table below shows the glass transition temperatures (DSC) according to different curing cycles. TG Shore D Hardness TG Shore D Hardness TG measured by DSC, 10°C/min, inflection point Hardness : ISO 868 MECHANICAL PROPERTIES Systems FLEXION Modulus Maximum strength Elongation at yield FLEXION Modulus Maximum strength Elongation at yield Measurements on pure resin according to the following standard : ISO 178 Datasheet V5 06.01.2021 - / Previous...

Abrir o catálogo na página 4

HEALTH & SAFETY Skin contact must be avoided by wearing protective ni- trile gloves & overalls or other protective clothing. Eye protection should be worn to avoid risk of resin, hardener, solvent or dust entering the eyes. If this occurs flush the eye with water for 15 minutes, holding the eyelid open, and seek medical attention. TRANSPORT & STORAGE Keep containers sealed and away from heat and cold preferably between 10°C and 30°C in a well ventilated area. Our products are guaranteed in their original pac- Ensure adequate ventilation in work areas. Respiratory protection should be worn...