SE 200 200°C TG STRUCTURAL EPOXY PREPREG ¬ Excellent handling, drape and mould conformance Excellent mechanical performance Fast, flexible curing options Suitable for compression moulding, autoclave or vacuum bag processing Achieves a Tg > 200°C (392°F) after press curing in 15 minutes at 195°C (383°F) Excellent hot-wet performance INTRODUCTION SE 200 is a high strength toughened epoxy system that has a flexible cure envelope ranging from 135°C (275°F) to 200°C (392°F). SE 200 has been developed to enable rapid part manufacture through a number of composite processing methods. The minimum cure temperature is 135°C (275°F) from which SE 200 develops a Tg and mechanical properties associated with higher temperature curing systems. Higher temperature cures in excess of 180°C (356°F) will achieve the best dry and wet thermal performance. Using the appropriate press moulding technology it is possible to achieve a 15 minutes hot-in / hot-out cure at 195°C (383°F), making SE 200 suitable for the economic production of automotive parts. SE 200 structural prepreg can be used in the making of parts such as structural lower tubs, bulkheads, front and rear scuttles, gearbox tunnels and other structural components.

Abrir o catálogo na página 1

PRODUCT INFORMATION SE 200 structural epoxy prepreg is available in a range of product formats. Please consult your local sales contact for further information. Full contact details can be found at www.gurit.com. PREPREG PROPERTIES RHEOLOGY DATA TRANSPORT & STORAGE SE 200 resin viscosity profile conducted at 1°C (2°F)/ minute. When stored sealed & out of direct sunlight. Minimum Viscosity STORAGE TEMP Temperature at Minimum Viscosity All prepreg materials should be stored in a freezer when not in use to maximise their useable life, since the low temperature reduces the reaction of resin and...

Abrir o catálogo na página 2

LAMINATE PROPERTIES CURED RESIN PROPERTIES Oven cured using standard processing techniques and a minimum cure time of 90 minutes at 135°C (275°F). PROPERTY TEST STANDARD Tensile Strength Tensile Modulus Flexural Strength Flexural Modulus Compressive Strength UNIDIRECTIONAL LAMINATE PROPERTIES Cured using standard processing techniques and a minimum cure time of 90 minutes at 135°C (275°F). PROPERTY Filament per tow TEST STANDARD Fibre Density Fibre Modulus Fibre Strength Resin Content Cure Method Cure Schedule Glass Transition Temperature 0° Tensile Cured Fibre Volume* 0° Tensile Strength...

Abrir o catálogo na página 3

WOVEN LAMINATE PROPERTIES Cured using standard processing techniques and a minimum cure time of 90 minutes at 135°C (275°F). PROPERTY TEST STANDARD Fabric / Fibre Description 400g/m 2x2 twill fabric using T300 3K fibre 200g/m 2x2 twill fabric using M46J 6K fibre 200g/m 2x2 twill fabric using T800 6K fibre Resin Content Cure Method Cure Schedule Glass Transition Temperature 0° Tensile Fibre Volume* 0° Tensile Strength (Normalised to 48%) 0° Tensile Modulus (Normalised to 48%) 90° Tensile Fibre Volume* 90° Tensile Strength (Normalised to 48%) 90° Tensile Modulus (Normalised to 48%) 0° Comp...

Abrir o catálogo na página 4

NOTICE All advice, instruction or recommendation is given in good faith but the Company only warrants that advice in writing is given with reasonable skill and care. No further duty or responsibility is accepted by the Company. All advice is given subject to the terms and conditions of sale (the Conditions) which are available on request from the Company or may be viewed at the Company’s Website: www.gurit.com/terms-and-conditions.aspx. The Company strongly recommends that Customers make test panels and conduct appropriate testing of any goods or materials supplied by the Company to ensure...