ZOLTEK™ PX35 Uni-Directional Fabrics

Product catalog summary

Description: ZOLTEK PX35 Stitch-Bonded Uni-Directional Carbon Fabrics are made from ZOLTEK PX35 50K Continuous Tow Carbon Fiber. They utilize unique fiber spreading techniques to offer a range of fabric weights suitable for various composite applications, enabling cost-effective and quick composite part build-up.

Material Overview: The fabrics are available in different weights (UD150 to UD900V) with varying carbon and glass fiber content. The total fabric weight ranges from 182 g/m² to 900 g/m². An epoxy resin binder is available upon request.

Fabric Construction: The fabrics offer various stitch lengths and patterns to meet application needs. Cured thickness per ply ranges from 0.21 mm to 1.00 mm, with roll widths of 30 cm to 122 cm and lengths of 30 m to 100 m.

Typical Packaging: Fabrics are wound on a cardboard cone, sealed in a polyethylene bag, and placed in a cardboard box. Rolls are stacked horizontally on pallets for shipping. Custom widths and lengths can be specified in purchase orders.

Certification: ZOLTEK PX35 Fabrics are manufactured according to ZOLTEK's published data, with a Certificate of Conformance provided with each shipment.

Safety: Users should read and understand the Material Safety Data Sheet (SDS) before using the product.

Approval: The fabrics are approved by DNV-GL for use in wind energy applications (Approval No. WP 1030011 HH).

Composite Properties: The fabrics exhibit a tensile strength of 1,600 MPa and a tensile modulus of 120 GPa. Compressive strength is 1,000 MPa with a compressive modulus of 110 GPa. The typical fiber volume fraction is 55% using a standard epoxy resin system.

Catalog excerpts

Technical Datasheet ZOLTEK™ PX35 Uni-Directional Fabrics Stitch-Bonded Uni-Directional Carbon Fabrics DESCRIPTION ZOLTEK PX35 Stitch-Bonded Uni-Directional Carbon Fabrics are produced from our ZOLTEK PX35 50K Continuous Tow Carbon Fiber. Unique fiber spreading techniques are utilized to obtain a wide range of UD fabric weights for a varied set of composite part applications. Quick composite part buildup is cost effectively achieved with our diverse weight range of low-cost carbon fabric products. MATERIAL OVERVIEW Polyester Veil Polyester Stitch 76 dtex Total Fabric Weight FABRIC CONSTRUCTION Stitch Length A variety of stitch lengths are available to meet application requirements. Stitch Pattern A variety of stitch patterns are available to meet application requirements. Cured Thickness/Ply Roll Width Roll Length 30 m Average Values Shown The properties listed in this datasheet do not constitute any warranty or guarantee of values. This information should only used for the purposes of material selection. Please contact us for more details. ZOLTEK™ PX35 ZOLTEK Corporation | 3101 McKelvey Road | Bridgeton, MO 63044 P: 314-291-5110 | F: 314-291-853

Open the catalog to page 1

Technical Datasheet ZOLTEK™ PX35 Uni-Directional Fabrics Stitch-Bonded Uni-Directional Carbon Fabrics COMPOSITE PROPERTIES Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Typical Fiber Volume Fraction (FVF) is 55%. Standard Epoxy Resin System The properties listed in this datasheet do not constitute any warranty or guarantee of values. This information should only used for the purposes of material selection. Please contact us for more details. TYPICAL PACKAGING Wound on cardboard cone, sealed in polyethylene bag, and placed in cardboard box. Rolls stacked horizontally...

Open the catalog to page 2

ZOLTEK™ PX35 Uni-Directional Fabrics

ZOLTEK™ PX35 Uni-Directional Fabrics

Catalog excerpts

All Zoltec catalogs and brochures

Archived catalogs