Panex® 35 Uni-Directional Fabrics

Product catalog summary

Description: The Panex® 35 Stitch-Bonded Uni-Directional Carbon Fabrics are made from Panex® 35 50K Continuous Tow Carbon Fiber. These fabrics utilize unique fiber spreading techniques to offer a wide range of fabric weights suitable for various composite applications, enabling cost-effective and quick composite part build-up.

Material Overview: The fabrics consist of 0° Carbon Panex® 35 50K, 90° Glass 34 dtex, Polyester Veil, Polyester Stitch 76 dtex, and Binder Resin Powder. The total fabric weight varies from 182 g/m2 to 900 g/m2, depending on the specific product variant (UD150 to UD900V).

Fabric Construction: The fabrics feature different stitch lengths, patterns, and cure thicknesses, with roll widths ranging from 30 cm to 122 cm and roll lengths from 30 m to 100 m. The stitch pattern includes Tricot and ½ Tricot.

Certification: The fabrics are manufactured according to Zoltek’s standards and come with a Certificate of Conformance. They are ISO 9001 and AS9100 certified by Bureau Veritas.

Packaging: Fabrics are wound on a cardboard cone, sealed in a polyethylene bag, and placed in a cardboard box. Rolls are stacked horizontally on pallets for shipping. Custom widths and lengths can be specified in purchase orders.

Safety: Users must obtain and understand the Material Safety Data Sheet (MSDS) before using the product.

Composite Properties: The fabrics have a tensile strength of 1,449 MPa, tensile modulus of 126 GPa, compressive strength of 809 MPa, and compressive modulus of 107 GPa. These properties are measured using DIN EN ISO 527 and ASTM standards.

Approval: The Panex® 35 Uni-Directional Fabrics are approved by Germanischer Lloyd for use in wind energy applications, with a typical fiber volume fraction of 55% using a standard epoxy resin system.

Catalog excerpts

Technical Datasheet Panex® 35 Uni-Directional Fabrics Stitch-Bonded Uni-Directional Carbon Fabrics Description Panex® 35 Stitch-Bonded Uni-Directional Carbon Fabrics are produced from our Panex® 35 50K Continuous Tow Carbon Fiber. Unique fiber spreading techniques are utilized to obtain a wide range of UD fabric weights for a varied set of composite part applications. Quick composite part build-up is cost effectively achieved with our diverse weight range of low-cost carbon fabric products. Material Overview Polyester Veil Polyester Stitch 76 dtex Binder Resin Powder Total Fabric Weight Average values shown Fabric Construction Stitch Length Stitch Pattern Cure Thickness Roll Width Roll Length 30 m Average values shown Zoltek Corporation | 3101 McKelvey Rd. | St. Louis, MO 63044 P: 314-291-5110 | F: 314-291-8536 | E: [email protected] | W: www.zoltek.com

Open the catalog to page 1

Panex® 35 Uni-Directional Fabrics Composite Properties Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus ASTM D695 Typical Fiber Volume Fraction (FVF) is 55%. Standard Epoxy Resin System Typical Packaging Wound on cardboard cone, sealed in polyethylene bag, and placed in cardboard box. Rolls stacked horizontally on pallets when shipping. Panex® 35 Fabrics are manufactured in accordance with Zoltek’s written and published data. A Certificate of Conformance is provided with each shipment. + Requirements other than standard widths and roll lengths should be specified by purchase...