TANKGUARD® EPOXY POLYAMIDE
4Pages

Protective & Marine Coatings EPOXY POLYAMIDE N11-100 SERIES PRODUCT DESCRIPTION RECOMMENDED USES TANKGUARD EPOXY POLYAMIDE is an epoxy polyamide coating formulated for application on steel surfaces in shipboard fuel and salt water ballast tanks. This product complies with Military Specication MIL-PRF-23236 Type V, Class 5, Grade C. For use over prepared substrates in marine and industrial environments: • Complies with Military Specication MIL-PRF-23236, Type V, Class 5, Grade C. • Marine vessels • Ballast Tanks • Fuel Tanks • Salt Water Tanks PRODUCT CHARACTERISTICS PERFORMANCE CHARACTERISTICS Primer-Green (No. 1) Finish-Blue (No. 3), Red, Gray, White Volume Solids: Weight Solids: Color Primer: Matte Green (No. 1), Part A Hardener for Primer, Part B Finishes: Blue (No. 3), Part A Hardener for Blue, Part B Recommended Spreading Rate per coat: Wet mils (microns) Dry mils (microns) ~Coverage sq ft/gal (m2/L) Red, Part A Hardener for Red, Part B Gray, Part A White, Part A Hardener for Gray and White, Part B Theoretical coverage sq ft/gal 944 23.1 (m2/L) @ 1 mil / 25 microns dft NOTE: Brush or roll application may require multiple coats to achieve maximum lm thickness and uniformity of appearance. Dry to touch: To recoat: minimum: minimum (non-epoxy)*: maximum: Cure to service: *An anti-foulant topcoat must be applied before the previous epoxy topcoat has hardened and while the epoxy is in a slightly tacky condition. This overcoat period is mainly dependent on the existing environmental conditions. If the epoxy is not tacky, an additional coat of epoxy must be applied to provide the required tacky condition. Pot Life: 4 hours at 77°F/25°C, 50% RH Sweat-in-Time: @ 35-60°F (1.6-16°C): 2 hours @ 61-70°F (16-21°C): 1-1.5 hours @ 71-90°F (21-32°C): 30 minutes - 1 hour @ 90°F+ (32°C+): none Shelf Life: Flash Point: Reducer/Clean Up: 36 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C) 100°F (38°C), SETA Flash, mixed Reducer #130, R7K130 Note: Flash point of reducer must be >100°F (38°C).

Protective & Marine Coatings EPOXY POLYAMIDE N11-100 SERIES PRODUCT INFORMATION SURFACE PREPARATION RECOMMENDED SYSTEMS Dry Film Thickness / ct. Mils (Microns) Steel, immersion*: 1 ct. TankGuard Primer (N11G100/N11V100) 1-2 cts. TankGuard Finish (N11 Series) Steel, atmospheric: 1 ct. TankGuard Primer (N11G100/N11V100) 2 cts. MIL-PRF-24635 Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Refer to product Application Bulletin for detailed surface preparation information. Minimum...

Protective & Marine Coatings EPOXY POLYAMIDE N11-100 SERIES APPLICATION BULLETIN APPLICATION CONDITIONS SURFACE PREPARATIONS Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Iron & Steel (immersion service) Remove all oil and grease from surface by Solvent Cleaning per SSPC-SP1. Minimum surface preparation is Near White Metal Blast Cleaning per SSPC-SP10/NACE 2. Blast clean all surfaces using a sharp, angular abrasive for optimum surface prole (1-3 mils / 25-75 microns). Remove all...

Protective & Marine Coatings EPOXY POLYAMIDE N11-100 SERIES APPLICATION BULLETIN APPLICATION PROCEDURES PERFORMANCE TIPS Surface preparation must be completed as indicated. Stripe coat all crevices, welds, and sharp angles to prevent early failure in these areas. Mix contents of each component thoroughly with low speed power agitation. Make certain no pigment remains on the bottom of the When using spray application, use a 50% overlap with each pass can. Then combine one part by volume of Part A with one part by volume of Part B. Thoroughly agitate the mixture with power of the gun to avoid...