SEAGUARD® MP MULTI-PURPOSE EPOXY PRIMER
4Pages

SEAGUARD® MP Protective & Marine Coatings MULTI-PURPOSE EPOXY PRIMER PART A PART B N12Y200 N12V200 YELLOW HARDENER Revised 8/10 9.36 PRODUCT DESCRIPTION RECOMMENDED USES SeaGuard MP - Multi-Purpose Epoxy Primer is a high performance, low VOC primer that is designed to be used over a variety of substrates. This product contains an anticorrosive pigment specically for the rst coat on non-iron/steel substrates, providing outstanding adhesion and enhancing dielectric properties with additional epoxy topcoats.This may be used in immersion service with recommended topcoats. • Corrosion resistant • Provides dielectric properties when used within an epoxy coating system • Contains high molecular weight epoxies • Contains hygroscopic solvent system May be used as a primer over multiple substrates such as: · Stainless steel · Aluminum · Galvanizing Ideal for marine environments May be used as a primer under an epoxy coating system for tanks containing fuel, brine, and non-potable water May be used on underwater aluminum hulls as the rst coat anticorrosive epoxy primer in combination with the recommended epoxy primer topcoats and recommended antifouling coatings. * PRODUCT CHARACTERISTICS PERFORMANCE CHARACTERISTICS * Use adequate cathodic protection for copper based antifouling paints. Finish: Flat • Abrasion resistant Color: Yellow • Outstanding adhesion Volume Solids: 62% ± 2%, mixed • Corrosion resistant Weight Solids: 76% ± 2%, mixed • Impact resistant VOC (EPA Method 24): <340 g/L; 2.80 lb/gal • Compatible with multiple substrates Mix Ratio: 1:1, by volume Epoxy coatings may darken or yellow following application and curing. Recommended Spreading Rate per coat: Wet mils (microns) Dry mils (microns) ~Coverage sq ft/gal (m2/L) Minimum 5.0 125 3.0 75 248 6.0 Maximum 7.0 175 4.0 100 330 8.1 Theoretical coverage sq ft/gal 992 24.3 (m2/L) @ 1 mil / 25 microns dft NOTE: Brush or roll application may require multiple coats to achieve maximum lm thickness and uniformity of appearance. Drying Schedule @ 5.0 mils wet (125 microns): @ 50°F/10°C To touch: 6 hours To recoat: minimum: 10-12 hours maximum: 30 days To cure: 14 days @ 77°F/25°C 50% RH @ 110°F/43°C 1 hour 30 minutes 4-6 hours 30 days 7 days 1-2 hours 30 days 7 days If maximum recoat time is exceeded, abrade surface before recoating. Drying time is temperature, humidity, and lm thickness dependent. Pot Life: Sweat-in-Time: 8 hours 1 hour Shelf Life: Flash Point: Reducer/Clean Up: 6 hours 30 minutes 1-2 hours 15 minutes 24 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C) 100°F (38°C) PMCC R7K130 www.sherwin-williams.com/protective continued on back

SEAGUARD® MP Protective & Marine Coatings MULTI-PURPOSE EPOXY PRIMER PART A PART B N12Y200 N12V200 YELLOW HARDENER PRODUCT INFORMATION 9.36 SURFACE PREPARATION RECOMMENDED SYSTEMS Dry Film Thickness / ct. Mils (Microns) Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Stainless Steel, Immersion: 1 ct. SeaGuard MP Epoxy Primer 1-2 cts. SeaGuard 5000 HS Epoxy 2 cts. SeaGuard Antifouling 3.0-4.0 (75-100) 4.0-7.0 (100-175) 4.0-7.0 * (100-175) Refer to product Application Bulletin for...

SEAGUARD® MP Protective & Marine Coatings MULTI-PURPOSE EPOXY PRIMER PART A PART B N12Y200 N12V200 YELLOW HARDENER APPLICATION BULLETIN APPLICATION PROCEDURES 9.36 PERFORMANCE TIPS Surface preparation must be completed as indicated. Stripe coat all crevices, welds, and sharp angles to prevent early failure in these areas. Mix contents of each component thoroughly with low speed power agitation. Make certain no pigment remains on the bottom of the When using spray application, use a 50% overlap with each pass cans. Then combine one part by volume of Part A with one part by volume of Part B....