N51R301 / N51B301
4Pages

Protective SEAVOYAGE® COPPER FREE ANTIFOULING PAINT & Marine N51R301 R Coatings N51B301 B ED PRODUCT DESCRIPTION RECOMMENDED USES SEAVOYAGE COPPER FREE ANTIFOULING PAINT is a solvent based, copper and tin free ablative antifoulant coating that deters soft and hard fouling. • Where a no copper discharge level antifoulant is required • Where a tin free, copper free, heavy metal free antifoulant is required • Where a low weight antifoulant is required. This product weighs approximately 2/3 that of traditional copper based antifoulants • Can be used over prepared existing antifouling systems • Acceptable for use on aluminum hulls • Service life of the coating is proportional to film thickness • Contains unique metal free organic biocide technology to comply with IMO ban on coatings containing TBT • Biocides are non-persistent in the environment • Low VOC to comply with environmental regulations • EPA Registration Number: 577-570 • Qualified to MIL-PRF-24647, Type I, Class 1 and 2, Grade A and B, Application 1 PERFORMANCE CHARACTERISTICS PRODUCT CHARACTERISTICS Finish: Volume Solids: Weight Solids: Test Name Adhesion Test Method ASTM D4541-02 Four year Fouling Rating ASTM D3623, Total immersion, Seawater, Ponce Inlet, FL Results 900 psi Rating 10 for general performance, Mollusks, Bryozoans, Amphipoda; Trace (<1% coverage) Barnacles, Anvelids, Hydroids, Algae Recommended Spreading Rate per coat: Wet mils (microns) Dry mils (microns) ~Coverage sq ft/gal (m2/L) Theoretical coverage sq ft/gal 1040 (25.5) (m2/L) @ 1 mil / 25 microns dft NOTE: Brush or roll application may require multiple coats to achieve maximum film thickness and uniformity of appearance. *See Performance Tips Drying Schedule @ 4.0 mils wet (100 microns): @ 40°F/4.5°C • Are non-persistent in the environment • Low solubility in water • Controls fouling organisms without the environmental impact to water quality or sediment associated with traditional metal based antifoulants • Product controls a broad spectrum of fouling • Service life of the coating is proportional to film thickness • Three hour hydrolytic half-life in seawater @ 77°F/25°C • Can be specified for dry-dock intervals up to 5 years Drying time is temperature, humidity, and film thickness dependent. Shelf Life: Flash Point: Reducer/Clean Up: 24 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C) 102°F (39°C) PMCC VM&P Naphtha, R1K3 or High Flash Napht

Protective SEAVOYAGE® COPPER FREE ANTIFOULING PAINT & Marine N51R301 R Coatings N51B301 B ED PRODUCT INFORMATION SURFACE PREPARATION RECOMMENDED SYSTEMS Dry Film Thickness / ct. Mils (Microns) Steel and Aluminum: 2 cts. SeaGuard 5000 HS 2-3 cts. SeaVoyage Copper Free AF Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Refer to product Application Bulletin for detailed surface preparation information. Other acceptable primers: SeaGuard 6000 Macropoxy 646 Aluminum: 1 ct. SeaGuard MP 1...

Protective SEAVOYAGE® COPPER FREE ANTIFOULING PAINT & Marine N51R301 R Coatings N51B301 B ED APPLICATION BULLETIN APPLICATION CONDITIONS SURFACE PREPARATIONS Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Iron & Steel Minimum surface preparation is Near White Metal Blast per SSPCSP10. Remove all oil and grease from surface by Solvent Cleaning per SSPC-SP1. Blast clean all surfaces using a sharp, angular abrasive for optimum surface profile (2 mils / 50 microns). Remove all weld...

Protective SEAVOYAGE® COPPER FREE ANTIFOULING PAINT & Marine N51R301 R Coatings N51B301 B ED APPLICATION BULLETIN APPLICATION PROCEDURES PERFORMANCE TIPS Surface preparation must be completed as indicated. When using spray application, use a 50% overlap with each pass of the gun to avoid holidays, bare areas, and pinholes. If necessary, cross spray at a right angle Mixing Instructions: Mix paint thoroughly to a uniform consistency with low speed power agitation prior to use. Spreading rates are calculated on volume solids and do not include an application loss factor due to surface profile,...