FAST CLAD® BRUSH GRADE EPOXY
4Pages

FAST CLAD® BRUSH GRADE EPOXY Protective & Marine Coatings PART A PART B B62W240 B62V240 WHITE HARDENER Revised 5/12 9.51 PRODUCT DESCRIPTION RECOMMENDED USES Fast Clad Brush Grade Epoxy is a high solids epoxy amine coating that is engineered specically as a brushable repair coating for Fast Clad ER Epoxy in sea water and fuel ballast tanks. The rapid return to service and high build of Fast Clad Brush Grade Epoxy provides superior protection compared to conventional epoxies. • Fast return to service • Low VOC • Extended pot life • Easy mixing For use as a brushable repair coating for Fast Clad ER Epoxy. For use in various exposures, including: • Ballast tank interiors • Fuel tanks • Sea water tanks • Petrochemical tanks • Approved by the U.S. Navy as a touch-up coating for Fast Clad ER PRODUCT CHARACTERISTICS Finish: Gloss Color: White Volume Solids: 83%, ± 2%, mixed Weight Solids: PERFORMANCE CHARACTERISTICS 90%, ± 2%, mixed Substrate*: Steel Surface Preparation*: SSPC-SP10/NACE 2 Surface Coating*: Fast Clad ER Epoxy System Tested*: 1 ct. Fast Clad Brush Grade Epoxy @ 8.0-10.0 mils (200-250 microns) dft VOC (EPA method #24): <150 g/L 1.25 lb/gal mixed (24 hour induction) Mix Ratio: 1:1 by volume Recommended Spreading Rate per coat: Wet mils (microns) Dry mils (microns) ~Coverage sq ft/gal (m2/L) Minimum 10.0 (250) 8.0 (200) 157 (3.8) Maximum 12.0 (300) 10.0 (250) 196 (4.8) Theoretical coverage sq ft/gal 1328 (32.5) (m2/L) @ 1 mil / 25 microns dft NOTE: Brush or roll application may require multiple coats to achieve maximum lm thickness and uniformity of appearance. Drying Schedule @ 10.0 mils wet (250 microns): @ 77°F/25°C 50% RH To touch: To handle: To recoat: Foot trafc: Cure to service: 3 hours 6.5 hours 4 hours 6.5 hours 24 hours *unless otherwise noted below Test Name Abrasion Resistance Adhesion Direct Impact Resistance Flexibility Pencil Hardness Test Method ASTM D4060, CS17 wheel, 1000 cycles, 1 kg load ASTM D4541 Results ASTM D2794 20 in. lb. ASTM D522 ASTM D3363 1/2" H 12.1 mg loss 920 psi Immersion (ambient temperature) for the following: • Ballast tank mix • Fresh water • Sea water • Petrochemicals Epoxy coatings may darken or yellow after application and curing. Drying time is temperature, humidity, and lm thickness dependent. Pot Life: Sweat-in-Time: Shelf Life: Flash Point: Reducer: Clean Up: 25 minutes (two qt mass) Not required 24 months, unopened Store indoors at 40°F (4.5°C) to 100°F (38°C) 100°F (38°C), PMCC, mixed Not recommended MEK, R6K10 or R7K104 www.sherwin-williams.com/protective continued on back

FAST CLAD® BRUSH GRADE EPOXY Protective & Marine Coatings PART A PART B B62W240 B62V240 WHITE HARDENER PRODUCT INFORMATION SURFACE PREPARATION RECOMMENDED SYSTEMS Dry Film Thickness / ct. Mils (Microns) Steel: 1 ct. Fast Clad ER 1 ct. Fast Clad Brush Grade 9.51 18.0-22.0 (450-550) 8.0-10.0 (200-250) The systems listed above are representative of the product's use, other systems may be appropriate. Surface must be clean, dry, and in sound condition. Remove all oil, dust, grease, dirt, loose rust, and other foreign material to ensure adequate adhesion. Refer to product Application Bulletin...

FAST CLAD® BRUSH GRADE EPOXY Protective & Marine Coatings PART A PART B B62W240 B62V240 WHITE HARDENER APPLICATION BULLETIN APPLICATION PROCEDURES 9.51 PERFORMANCE TIPS Surface preparation must be completed as indicated. Stripe coat all crevices, welds, and sharp angles to prevent early failure in these areas. Mixing Instructions: Mix contents of each component thoroughly using low speed power agitation. Make certain no pigment remains on the bottom or the sides of the can. Then combine one part by volume of Part A with one part by volume of Part B. Thoroughly agitate the mixture with power...