SEAJET 040 SHŌSHA
1 / 2Pages

SEAJET 040 SHŌSHA Product description SEAJET 040 SHŌSHA is a copper-free, super self polishing antifouling based on an unique resin that gives outstanding antifouling protection in the highest fouling areas. The excellent antifouling effect is derived from the highly active hydrolysis polymer which ensures maximum effectiveness and leaching of active ingredients. Can be used on all substrates including aluminium. Product data Colour White, navy blue, black. Flash point Volume solids % Pack sizes Mixing ratio Application details Thinner Application methods Brush, roller Ambient temperature Product temperature Substrate temperature Spreading rate Recommended film thickness Wet (µm) 100 per coat Dry (µm) 40 Substrates For use over suitably primed GRP, wood, steel, aluminium. Preceding coating SEAJET 015 Underwater Primer, SEAJET 117 Multipurpose Epoxy Primer. Subsequent coating Before use, stir thoroughly until product is mixed to a uniform consistency. * Film thickness and spreading rate depends on application method, more layers may be required to achieve the specified film thickness. Values are based on roller application. Maximum immersion time after application is 6 months. After immersion, SEAJET 040 SHŌSHA may exhibit a slight colour change. Colour difference between batches may occur. Mix different batches before use. Surface preparation Over existing antifouling: high pressure fresh water wash (±200 bar) to remove any fouling and salt. Remove existing antifouling in poor condition. For existing antifouling in good condition, check the SEAJET antifouling compatibility table before applying. Ensure the surface is dry and free of contamination such as salt, grease or oil. Degrease if required. Apply two coats. Apply an extra coat on leading edges, waterline, rudders and stern gear. Antifoulings should only be wet sanded or chemically stripped. Never burn-off or dry sand old antifoulings. GRP/Steel: first sand with P100 abrasive paper, remove all dust and apply SEAJET 117. Wood: first sand with P100 abrasive paper, remove all dust and apply SEAJET 015. Aluminium: first sand with P100 abrasive paper, remove all dust and apply SEAJET 117.

SEAJET 040 SHŌSHA Drying / overcoating data Drying time Overcoating interval Surface dry:3 hours Hard dry 6 hours Induction time Surface dry:2 hours Hard dry 5 hours Surface dry:1 hour Hard dry 4 hours Surface dry:30 min Hard dry 3 hours Drying times and overcoating intervals will increase with increasing film thickness applied. Before re-coating, always check that the existing paint film is 'through' dry. General information Storage Store the containers in a dry, cool and well ventilated space and away from direct sunlight. Containers must be kept firmly closed. Handle with care....