SEAJET 038 TAISHO Product description Seajet 038 Taisho is a copper-free, super self polishing antifouling based on an unique resin that gives outstanding antifouling protection in the highest fouling areas. The excellent antifouling effect is derived from the highly active hydrolysis polymer which ensures maximum effectiveness and leaching of active ingredients. Can be used on all substrates including aluminium. Product data Colour Flash point Volume solids % VOC (Theoratical) Pack sizes Mixing ratio White, Mid blue, Navy blue, Bright Red, Black, Light Grey, Dark Grey. 29°C 40 ±2 Application details Thinner Application methods Conditions SEAJET THINNER A Brush, roller*, spray (professional use only) Spray details Spreading rate Recommended Film thickness per coat Substrates Preceding coating Subsequent coating Mixing Ambient temperature Max. humidity Product temperature Substrate temperature Nozzle tip Paint output pressure: Thinning: 10,0 Wet (pm) 100 Dry (pm) 40 For use over suitably primed GRP, wood, steel. SEAJET 015 Underwater Primer. When applying direct to SEAJET 117, apply within 48 hours. Before use, stir thoroughly until product is mixed to a uniform consistency. Notes * Film thickness and spreading rate depends on application method, more layers may be required to achieve the specified film thickness. Maximum immersion time after application is 6 months. After immersion, Seajet 038 Taisho may exhibit a slight colour change. Colour difference between batches may occur. Mix different batches before use. Surface preparation Over existing antifouling: High pressure fresh water wash (±200 bar) to remove any fouling and salt. Remove existing antifouling in poor condition. For existing antifouling in good condition, check the SEAJET antifouling compatibility table before applying. Ensure the surface is dry and free of contamination such as salt, grease or oil. Degrease if required. Apply two coats. Apply an extra coat on leading edges, waterline, rudders and stern gear. Antifoulings should only be wet sanded or chemically stripped. Never burn-off or dry sand old antifoulings. GRP/Steel: first sand with P100 abrasive paper, remove all dust and apply SEAJET 015 or SEAJET 117. Wood: first sand with P100 abrasive paper, remove all dust and apply SEAJET 015. Aluminium: first sand with P100 abrasive paper, remove all dust and apply SEAJET 017 followed by SEAJET 117.

SEAJET 038 TAISHODrying / overcoating data Temperature Notes: Note: Drying times and overcoating intervals will increase with increasing film thickness applied. Before re-coating, always check that the existing paint film is 'through' dry. General information Storage Store the containers in a dry, cool and well ventilated space and away from direct sunlight. Containers must be kept firmly closed. Handle with care. Transportation The product should stay in a securely closed container during transport. Shelf life Min. 2 years @ 20°C Disposal Do not empty into drains, dispose of this material and...