SEAJET 027 SAIKŌ Product description SEAJET 027 SAIKŌ is a copper free, self polishing antifouling paint based on an unique resin. Excellent antifouling performance with a co-biocide against slime. Available in bright colours including white. Can be used on all substrates including aluminium. Product data Colour White, Navy Blue, Black, Platinum Grey. Flash point Volume solids % Pack sizes Mixing ratio Application details Thinner Application methods Brush, roller, spray (professional use only)* Ambient temperature Product temperature Substrate temperature Paint output pressure: Spray details Spreading rate Recommended film thickness Wet (µm) 100 per coat Dry (µm) 40 Substrates For use over suitably primed GRP, wood, steel, aluminum. Preceding coating SEAJET 015 UNDERWATER PRIMER, SEAJET 117 MULTIPURPOSE EPOXY PRIMER. Subsequent coating Before use, stir thoroughly until product is mixed to a uniform consistency. * Film thickness and spreading rate depends on application method. Values are based on roller application. In case of brush application more layers may be required to achieve the specified film thickness. On immersion, SEAJET 027 SAIKŌ may exhibit a slight colour change. Colour difference between batches may occur. Mix different batches before use. Surface preparation Over existing antifouling: high pressure fresh water wash (±200 bar) to remove any fouling and salt. Remove existing antifouling in poor condition. For existing antifouling in good condition, check the SEAJET antifouling compatibility table before applying. Ensure the surface is dry and free of contamination such as salt, grease or oil. Degrease if required. Apply two coats. Apply an extra coat on leading edges, waterline, rudders and stern gear. Antifoulings should only be wet sanded or chemically stripped. Never burn-off or dry sand old antifoulings. GRP/Steel: first sand with P100 abrasive paper, remove all dust and apply SEAJET 015 or SEAJET 117. Wood: first sand with P100 abrasive paper, remove all dust and apply SEAJET 015. Aluminium: first sand with P100 abrasive paper, remove all dust and apply SEAJET 017 followed by SEAJET 117.

SEAJET 027 SAIKŌ Drying / overcoating data Drying time Overcoating interval Surface dry:3 hours Hard dry: 6 hours Induction time Surface dry:2 hours Hard dry: 5 hours Surface dry:1 hour Hard dry: 4 hours Surface dry:30 min Hard dry: 3 hours Note: Drying times and overcoating intervals will increase with increasing film thickness applied. Before re-coating, always check that the existing paint film is 'through' dry. * With Seajet 117 Multipurpose Epoxy Primer. General information Storage Store the containers in a dry, cool and well ventilated space and away from direct sunlight. Containers must...