SEAJET 039 PLATINUM mono component
2Pages

SEAJET 039 PLATINUM MONO-COMPONENT Product description Seajet 039 Mono-component is an ultimate performing SPC antifouling. Based on the latest resin technology from Japan it is suited to all fouling environments and ideal for application to boats in the highest fouling areas. Can be used on all substrates except aluminium. Product data Colour Black, graph.grey RAL 7024, greenish grey, light red, navy blue, mid blue Flash point Volume solids % Pack sizes Mixing ratio Application details Thinner Application methods Brush, roller, spray (professional use only)* Ambient temperature Product temperature Substrate temperature Paint output pressure: Spray details Spreading rate Recommended film thickness Wet (µm) 100 per coat Dry (µm) 44 Substrates For use over suitably primed GRP, wood, steel. Preceding coating SEAJET 015 Underwater Primer, SEAJET 117 Multipurpose Epoxy Primer. Subsequent coating Before use, stir thoroughly until product is mixed to a uniform consistency. * Film thickness and spreading rate depends on application method, more layers may be required to achieve the specified film thickness. Values are based on roller application. Maximum immersion time after application is 6 months. After immersion, Seajet 039 Platinum Mono may exhibit a slight colour change. Colour difference between batches may occur. Mix different batches before use. Surface preparation Over existing antifouling: high pressure fresh water wash (±200 bar) to remove any fouling and salt. Remove existing antifouling in poor condition. For existing antifouling in good condition, check the SEAJET antifouling compatibility table before applying. Ensure the surface is dry and free of contamination such as salt, grease or oil. Degrease if required. Apply two coats. Apply an extra coat on leading edges, waterline, rudders and stern gear. Antifoulings should only be wet sanded or chemically stripped. Never burn-off or dry sand old antifoulings. GRP/Steel: First, apply SEAJET 117. Wood: First, apply SEAJET 015 UNDERWATER PRIMER. Aluminium: DO NOT USE SEAJET 039 PLATINUM MONO-COMPONENT on aluminium surfaces.

SEAJET 039 PLATINUM MONO-COMPONENT Drying / overcoating data Drying time Overcoating interval Surface dry:3 hours Hard dry: 12 hours Induction time Surface dry:2 hours Hard dry: 8 hours Surface dry:1 hour Hard dry: 5 hours Surface dry:30 min Hard dry: 4 hours Drying times and overcoating intervals will increase with increasing film thickness applied. Before re-coating, always check that the existing paint film is 'through' dry. General information Storage Store the containers in a dry, cool and well ventilated space and away from direct sunlight. Containers must be kept firmly closed....