■ Adjustable pot life from 1h to 2h ■ Very low viscosity and high wetting power ■ TG: 85° to 130° depending on hardener used ■ Excellent cross linking properties even at low post-curing temperatures RESOLTECH 1800 is an advanced infusion and injection epoxy resin system with an extremely low viscosity for fast and safe wetout by infusion and injection. It features high mechanical properties, a TG of up to 130°C and up to 5H30 of infusion or injection time. A great property of the system is its constant low viscosity right until gel time. It therefore offers reliable impregnation and air release throughout the infusion or injection process. Suitable for very large composite parts. This system has excellent cross linking properties and enables to obtain a high TG of 130°C even at low post curing temperatures (15h @ 60°C). It is suitable for both tooling and parts manufacturing. Typical applications include large marine structures, wind turbine blades, moulds for pre-preg production. Monolitic carbon fibre infusions may be performed with fibre ratios of over 68% with 0,4% RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES

MIXING RATIO The mixing ratio must be respected neither excess nor default. The mixture should be homogeneous and The mixing ratio must be accurately measured. It is not possible to change the ratio, it would result in lower mechanical properties. The mixture should be thoroughly stirred to ensure full Thermosetting products generate heat when curing. The amount of heat generated varies with the hardener used, the temperature and the quantity of resin mixed. It is therefore necessary to only mix the necessary amount usable within the given pot life. Keeping the mixture in flat open containers...

PHYSICAL CARACTERISTICS (Continued...) Viscosities (mPa.s) according to ISO 12058-2 @ 23°C Evolution of initial viscosity vs. temperature according to ISO 12058-2 RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES

Temperature and Viscosity Vs Time on 70g (5cm) RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES

CURING & POST CURING The 1800 system, specially when used with the 1805 hardener should not be released from the mould without curing at intermediate temperatures of minimum 12h @ 40° or 6h @ 60° as it remains brittle without this initial cure. It will then require a minimal post curing of 15h to 60°C in order to reach its thermo mechanical properties While a postcure is not mandatory, in order to obtain a material at the maximum of its mechanical properties it is necessary to respect the following recommended cycles: The 60°C temperature cure means that the system does not need to be used in...

MECHANICAL CHARACTERISTICS Values on non reinforced resin after 7 days at 23°C Values on glass / epoxy composite after 7 days at 23°C * * Composite manufacturing Composite manufacturing was achieved by infusion on 16 layers of glass twill 2-2 of 285 g/m2 RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES

MECHANICAL CHARACTERISTICS (Continued...) Barcol Hardness: WATER ABSORPTION Water absorption at 23°C during 24h according to ISO 62 is : Reinforced resin: Water absorption at 23°C during 24h according to ISO 62 is : RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES

HEALTH & SAFETY The usual precautions for the use of epoxy resins must be respected. Our health and safety datasheets are available upon request. It is important to wear protective clothing and avoid skin contact with the products. In case of contact, wash thoroughly with soap and water. In case of eye contamination, wash thoroughly with warm water. Consult a specialist. TRANSPORT & STORAGE Keep containers sealed and away from heat and cold preferably between 10°C and 30°C in a well ventilated area. Shelf life is one year in sealed containers as Nota : The data provided in this document are provided...