Technical datasheet 02/06/2010 RESOLTECH 3050C & 3050CT Hardener 3054C & 3054CT Structural Epoxy Adhesive Structural epoxy adhesive for demanding applications Ambient temperature curing. 1/1 mixing ration in volume. Thixotropic version, 3050CT available for non-sag vertical surface applications. The Resoltech 3050C & 3050CT epoxy adhesive is a rubber toughened, high performance adhesive that will enable bondings with very high mechanical resistance (310 kg/cm2) and high peel-resistance It’s curing at ambient temperature and 1/1 mixing ratio in volume or 100:80 by weight makes of the 3050C &3050CT an easy product to work with. It will enables structural bondings of all types of composite materials, steel, aluminium, wood and will resist in a large range of operating temperatures from -50°C to +80°C, with a maximum service temperature of 140°C. It is a solvent less adhesive with no contraction upon curing. The 3050C/3054C is for horizontal applications only. The 3050CT/3054CT is a thixotrpic version that will enable bondings in all application conditions PHYSICAL ASPECT Density (at 25°C) Resin Hardener Mix Visual aspect: Resin Hardener Viscosity, Brookfield at 25°C Resin Hardener Mix: 1,18 gr/cm3 0,96 gr/cm3 1.05 gr/cm3 Yellow viscous liquid Blue viscous liquid 35.000 mPa.s 50.000 mPas 40.000 mPas Page 1/3 RESOLTECH RESOLVING YOUR ENGINERING CHALLENGES www.resoltech.com

Open the catalog to page 1

Resin 3050C & 3050CT Hardener 3054C & 3054CT APPLICATION Mixing ratio by volume Mixing ratio by weight 1:1 100:80 Gel Time on 100g @ 25°C (TECAM) Gel Time on 250g @ 25°C (TECAM) Gel Time in film @ 25°C (TECAM) 118 min 75 min 4h Exothemic Peak on 100 gr. 113 °C RESOLTECH 3050C & 3054CT is an ambient temperature cure adhesive formulated for a large range ofb onding applications and will provide superior adherence onto composites, steel, aluminium, concrete and wood substrates. It is suitable for core bonding and also for composite to composite bonding. All surfaces should be clean, dust-free...

Open the catalog to page 2

Resin 3050C & 3050CT Hardener 3054C & 3050CT MECHANICAL PROPERTIES RESOLTECH 3050C &3050CT do not require a post cure, although a post cure at an elevated temperature (at 60°C for example) will improve mechanical properties and accelerate the cure. Fully cured mix after 7 days at ambient temperature: at 20°C : 7 days at 40°C : 48 hours at 60°C : 12 hours Tensile/shear strength: Cured for 24H @ 25°C Cured for 7 days @ 25°C Cured for 7 days @ 25°C + 2H @ 70°C 20N/mm2 29N/mm2 31N/mm2 TG Maximum service temperature TG after ambient temperature cure: Maximum TG after 2 h at 60 °C 140°C 50-55 °C...

Open the catalog to page 3