TECHNICAL DATA SHEET RESOLCOAT 3010T EPOXY HIGH BUILD SURFACER RESOLCOAT 3010T is a high build surfacer formulated to create a barrier against water and chemicals to protect a yacht hull as well as providing a perfect surface finish and interface for all marine topcoats. The system is easy to apply by spray, roller or brush and is fast drying. A suitable finish is obtained after at least two coats of this system. Suitable for steel, aluminium, GRP and wooden yachts. MIXING MIXING RATIO RESIN 3010T HARDENER 3014T BY VOLUME 4 1 BY WEIGHT 100 15 Hardener available: 3014T (replaces hardener 3015T). Thinner: RESOLTECH 3018 The resin component should be stirred mechanically prior to mixing with hardener. WARNING: The mixing ratio must be accurately followed. It is not possible to change the ratio, it would result in lower mechanical properties. The mixture should be thoroughly stirred to ensure full homogeneity. SURFACE PREPARATION RESOLCOAT 3010T should be applied onto a prepared surface (see TechNotes#10 for more application information). The surface should be clean, dust-free and degreased. RESOLCOAT 3010T will provide superior adherence onto GRP, metals, RESOLCOAT 8020EX and any laminate. Steel and aluminum surface should be prepared first and the coated with the RESOLCOAT 3010P primer. Defects deeper than 1,5 mm should be filled with 8020 EX filler prior to 3010T application APPLICATION Use above 10°C and minimum 3°C above dew point. Mix thoroughly the resin component before mixing with hardener. As for all solvent based products, wait for 30 min after mixing before application (maturing time). SPRAYING: Pressure required: Airless:150kg/cm2. Use 0.46/0.69mm nozzles thinned with RESOLTECH 3018 thinner at 10 to 15%. If sprayed without using thinner with a classic gravity spray gun, use a nozzle of 2,6 mm with min 4-6 bar air pressure. COVERAGE: 4m2 per kg. on average for a 100 microns dry layer (recommended amount/layer) Several layers can be applied until a fair surface is obtained (usually 2 coats ). No sanding is required between coats. Once cured, the filler can be sanded with an orbital sander. “Pinholes” should be treated with a mixture of Resolcoat 3010T and HP510 glassbubbles. Do not use another filler as it may create “hard points”. Avoid thick coats that may lead to solvent entrapment. Tools should be cleaned with acetone, thinner or any equivalent product.

Open the catalog to page 1

CURING Lower temperatures will increase curing time. In a cold environment it may be wise to install a temporary structure and use space heaters to increase temperature. High temperatures will speed up the cure. RESOLCOAT 3010T should be used in a well ventilated area. A good ventilation is the best way to ensure the solvent evaporates fast avoinding solvent entrapment Temperature 10°C Pot life Touch dry 23°C 35°C 16 hours/1 Litre 5H 2H 30MN 1H Re-coatable & sand- 16H able 8H 5H Full cure 7 Days 3 Days 14 Days The resolcoat 3010T does not need to be re-sanded before being recoated or...

Open the catalog to page 2