Fast Cure Epoxy Repair Compound Product description PSI-326 is a low-odor, two-component, modified epoxy adhesive that cures rapidly at room temper- ature with exceptional tensile adhesion and peel strength to a wide variety of substrates. In just a lew minutes PSI-326 forms a tough bond without the need for clamping. Thin sections may take somewhat longer. Basic uses adhesive to bond wood, metal, fiberglass, glass, ceramics and many hard plastics. It forms a water- resistant bond that is tough enough to be drilled. lapped, filed or sanded after final cure. ■ Maximum temperature range is 250°F (12TC) • Not intended for structural applications. Available in 2-lb. (907 gm) kits (see heat warning under "Mixing"). Special packaging available upon request. Performance Data* Uncured Properties Final mixed color Test Method shrink upon curing. • High peel strength household repairs. Application limitations Work life, 3 grams at 75°F (24°C) Non-volatile content Cure time to lap shear tensile Cure time to full cure at 75°F (24°C) Cured Mechanical Properties Tensile strength Lapshear tensile adhesive strength Compressive strength Upper temperature limits Cured Electrical Properties Insulation resistance Volume resistivity Dielectric strength • Typical properties aie lor information only no! lor Thixotropic paste

Open the catalog to page 1

Application Surface preparation: To achieve optimum adhesion, surfaces should be dry and free of grease or dirt. Scuffing or sanding the surface prior to cleaning helps insure a good bond. Mixing and application: Mix one part A with one part B by weight or volume until uniform. Do not mix more than 8 oz. (224 gm.) total, i.e., 4 oz. (112 gm) Part A and 4 oz. (112 gm.) Part B at one time. Material becomes very hot during cure. Use within 3 minutes of mixing. See Performance Data on reverse side. Health precautions • May irritate sensitive skin. Wash hands with soap and water after use. • Eye...

Open the catalog to page 2