Liquid Glass

Product catalog summary

Description: Liquid Glass Epoxy Resin is a high-strength laminating resin known for its excellent waterproofing and adhesive properties. It is water-clear when mixed and provides a clear gloss finish.

Uses: This resin is suitable for use with Dynel cloth, fiberglass, and other composite reinforcing materials. It is also used for bar tops, filling knot holes in timber, and decoupage applications.

Properties: At 20°C, the resin has a drying time of 1-2 hours for surface drying, reaching 90% cure in 24 hours and full cure in 7-10 days. The pot life is 15 minutes in mass or 30 minutes when spread out. The mixing ratio is 2:1 by volume, and it has a weight of 1.066 kg per liter when mixed.

Application: The resin is mixed by combining two volumes of resin with one volume of hardener, followed by thorough stirring. It is applied using a short nap paint roller and brush, with special instructions for pour-on applications.

Precautions: The resin is a mild skin irritant and may cause allergic reactions. Protective clothing and adequate ventilation are recommended. In case of ingestion, eye contact, or inhalation, specific first aid measures should be followed.

Special Instructions: For pour-on applications, calculate the area in square centimeters to determine the volume needed, with 1 mixed liter covering 1 square meter at 1 mm thickness.

Transportation and Sizes: Classified as dangerous goods class 3.2, it is available in various pack sizes ranging from 750 ml to 30 liters.

Disclaimer: Any advice or information provided by NORGLASS is given in good faith but without liability or responsibility.

Catalog excerpts

LIQUID GLASS EPOXY RESIN JULY 2014 PRODUCT DATA SHEET NORGLASS LABORATORIES PTY.LTD. A.B.N. 92 001 807 245 P.O. Box 312, Neutral Bay. NSW 2089 Australia 59 Moxon Road, Punchbowl NSW Ph: 61 2 9708 2200 Fax: 61 2 9796 3069 Email: [email protected] www.norglass.com.au LIQUID GLASS EPOXY RESIN DESCRIPTION: A high strength laminating resin with excellent waterproofing and adhesive properties. For use with Dynel cloth, fibreglass and other composite reinforcing materials, bar tops, knot holes in timber or for decoupage applications. Water -clear when mixed Clear gloss Varies according to reinforcing used and in pour-on applications. DRYING TIME: 1-2 hours (surface) 90% in 24 hours, 100% 7-10 days 500mls: 15 minutes in mass, 30 minutes if volume is spread out into a shallow tray or dish. MIXING RATIO: VOLUME SOLIDS: FLASH POINT: NORGLASS EPOXY THINNER

Open the catalog to page 1

LIQUID GLASS EPOXY RESIN None allocated (base), 1866 (Hardener) Refer to NORGLASS REINFORCING GUIDE for laminating usage. Varies according to reinforcing methods or other applications. Mixing is carried out by placing 2 equal volumes of resin into a clean container and then adding 1 equal volume of epoxy Hardener. Thorough stirring is essential. The mixed volume is then transferred to shallow paint trays to maximise the working time. Application is normally carried out with a short nap paint roller and clean paint brush. Pour on applications, see SPECIAL INSTRUCTIONS below. Hazchem 3[Y] P.G....