Perfection Finishes High Performance Polyurethane Gloss Finish PRODUCT DESCRIPTION Perfection 2part polyurethane is the ultimate performing, high gloss topside finish. It provides the longestlasting, ultrahigh gloss finish that has superb colour retention, together with excellent chemical and abrasion resistance. It has been formulated specifically to enable skilled amateur users to achieve professional quality results with ease. UV filters combined with the chemical cure of the polyurethane give the longest life possible. * Hardest, abrasionresistant finish making it an excellent choice for use on high wear areas e.g. decks (with NonSlip Additive). * Chemically resistant to diesel, petrol, oil, mild acids and alkalis PRODUCT INFORMATION Colour YHA183Platinum, YHA184Med. White, YHA192Off White, YHA194Oyster White, YHA198Mat'horn White, YHA216 Royal Blue, YHB000Snow White, YHB663Jade Mist Green, YHE294Chilli Red, YHF991Mauritius Blue, YHK990Flag Blue, YHS056Fight. Lady Yellow, YHS070Cream, YHS187Polar White, YHS248Arctic White, YHS253Pearl White, YHS299Rochelle Red, YHS936Lauderdale Blue, YHY999Jet Black High Gloss Specific Gravity Volume Solids Converter/Curing Agent Typical Shelf Life Unit Size 750 ml, 2.5 lt Note: Not all colours or pack sizes are available in all countries. Consult with your local Technical Representative for further information. DRYING/OVERCOATING INFORMATION Drying 10°C (50°F) PREVIOUSLY PAINTED SURFACES In Good Condition Wash down with Super Cleaner, rinse with fresh water and allow to dry. Abrade with 280320 grade (grit) paper. In Poor Condition Remove all previous coatings and prime the substrate. PRIMING See primer datasheets. BARE WOOD/STEEL/ALUMINIUM Prime with Interprotect. GRP Wash down with Super Cleaner, rinse with fresh water and allow to dry. Sweep blast or abrade with 180220 grade paper. No priming necessary. AGED/WEATHERED GELCOATS Due to increased porousness, the risk of solvent/moisture entrapment is increased, leading to potential blistering. To reduce this risk 3 coats of Interprotect are recommended to seal the gelcoat. Interprotect must be overcoated with Perfection Undercoat prior to topcoat application. ALL SUBSTRATES Use Perfection Undercoat. Sand the undercoat smooth with 320400 grade (grit) wet or dry paper. Remove dust with a tack rag. Apply 23 coats. Mixing Stir each part individually. Add Curing Agent to the Base, stir and leave for 10 minutes to allow bubbles to disperse. Thinner: Thinner No 9 Thinning: May be thinned between 510% to assist application. Cleaner:Thinner No 9. Ventilation and Humidity Control: Apply in dry, well ventilated conditions. Avoid excessively humid conditions, over 80% relative humidity. Other: Best applied at 15°C. For lighter colours, mix the first coat of finish 50:50 with the undercoat to improve the depth Please refer to your local representative or visit www.yachtpaint.com for further information. of colour and opacity. Both products should be mixed with respective curing agents first. For best results when applying All trademarks mentioned in this publication are owned by, or licensed to, the AkzoNobel group of companies. © AkzoNobel 2018. by roller, smooth off with a pad or brush. If using as a deck paint, mix in nonslip additive. Full hardness is achieved after 710 days at 15°C/59°F. If required, Perfection Matting Additive (YZM914) is available for use with Perfection. See Perfection Matting Additive datasheet for details on use. Ref:3110 Perfection Issue Date:

must be overcoated with Perfection Undercoat prior to topcoat application. ALL SUBSTRATES Use Perfection Undercoat. Method Sand the undercoat smooth with 320400 grade (grit) wet or dry paper. Remove dust with a tack rag. Apply 23 coats. Perfection Finishes High Performance Mixing Stir each part individually. Add Curing Agent to the Base, stir and leave for 10 minutes to allow bubbles to disperse. Thinner: Thinner No 9 Thinning: May be thinned between 510% to assist application. Polyurethane Gloss Finish Cleaner:Thinner No 9. Ventilation and Humidity Control: Apply in dry, well ventilated conditions....