ABLATIVE VINYL ANTIFOULING

ABLATIVE VINYL ANTIFOULING
2Pages

Catalog excerpts

ABLATIVE VINYL ANTIFOULING Description Tough and adhesive product, with a high antifouling performance. It quickly dries by solvent evaporation. It keeps the hull free from marine growth for longer and helps the boat to reach maximum speed. Fields of Application As an antifouling on any kind of submerged surfaces. Technical Data Finish 20 - 25 minutes / Immersion (Launching): after 12 hours and up to 6 months Brush, Roller. TITAN YATE Thinner Pack sizes Variations in temperature, humidity, thickness, tinting or surface type, etc. may lead to changes in drying, in coverage or in other properties. Directions for use GENERAL REMARKS: Carefully stir the contents in the can before use. The surface has to be sanded, clean, dry and salt-free (wash it). Do not paint if the surface is under direct sunlight or if it has dew on it. In areas of higher wear, such as waterline, keel, rudder, etc., it is recommended an additional coat, since water turbulence speeds up self-polishing. BARE SURFACES: Polyester:Degrease with TITAN YATE Thinner and apply 2 coats of TITAN YATE Epoxy Primer in intervals of 24 hours (For osmosis prevention, apply M-150 Epoxy Primer). Metal: Apply 1 coat of TITAN YATE Epoxy Primer. After 24 hours, apply 3-4 coats of TITAN YATE M-150 Epoxy Primer, strictly

Open the catalog to page 1

following the instructions of the pack. Wood: Apply 2 coats of TITAN YATE Epoxy Primer, the 1st coat thinned with 20% TITAN YATE Thinner. In all cases, finish with two coats of TITAN YATE Antifouling. MAINTENANCE OF PREVIOUSLY COATED SURFACES IN GOOD CONDITION: Wash with fresh water jet and directly apply 2 coats of TITAN YATE Self-Polishing Antifouling. If the previous coats are not vinylbased, thoroughly remove them with TITAN Paint Stripper or TITAN YATE Water-Based Paint Stripper. Wash with fresh water and afterwards proceed as for a bare surface. MAINTENANCE OF PREVIOUSLY COATED...

Open the catalog to page 2