IJMOPOX ZF PRIMER

Catalog excerpts

DESCRIPTION IJmopox ZF Primer is a general purpose, two component primer based on epoxy resin and apolyamide hardener. PRINCIPAL CHARACTERISTICS • Contains zinc phosphate as corrosion inhibitor; • Recommended as primer in paint systems for the protection of steel, aluminium, wood, etc.; • Excellent anti corrosion properties; • Excellent adhesion to plastics and GRP; • Suitable to repair small hair cracks and eliminate micro porosity in GRP; • May be recoated with both two component or conventional coatings, even after a long weathering interval; • Excellent mechanical properties; • Application and curing at temperatures as low as 5 ˚C and relative humidifies as high as 90%; • Excellent resistance to various chemicals and (sea) water; • Easy to apply by brush or spray. COLOURS AND GLOSS Off-white - Eggshell BASIS PROPERTIES (AT Density Solid content Recommended d.f.t. Dust dry after Full cure after Recoating interval 23˚C AND 50% R.H.) : approx. 1,4 g/cm3 : approx. 55 % (volume) : 50 - 100 µm (depending on application), see additional information : approx. 2 hours : approx. 5 days, see additional information : min. 16 hours, see additional information max. unlimited, provided clean and dry Shelf life : separate components, stored cool and dry in original packaging, minimum 12 months Flash point (DIN53213) : base component 25 ºC hardener 30 ºC SPREADING RATE at 50 µm (d.f.t.) : 11,0 m2/l at 75 µm (d.f.t.) : 8,3 m2/l at 100 µm (d.f.t.) : 5,5 m2/l The practical spreading rate depends on a number of variables, such as: shape and size of object to be painted, the condition and profile of the substrate, the method of application, climatologic conditions and skill of labour. SUBSTRATE CONDITION AND TEMPERATURE Steel : preferably grit blasted to ISO Sa 2½ or powertool cleaned to ISO St 3 (grit paper P24-36); Aluminium : sanded wit grit paper P60-80; Wood : moisture content maximum 12%, sanded with grit paper P120-180; Reinforced polyester : dry, sanded with grit paper P120-180; Previous coatings : two component coatings, clean and dry, in good condition, free from any contamination and loose particles, sanded with grit paper P80. IJmopox ZF primer is not compatible with one component coatings; Other substrates : clean and dry, in good condition, free from any contamination and loose particles, sanded with grit paper P80. During application and curing a minimum temperature of 5 ºC is allowed. The temperature of the substrate should be mi

 Open the catalog to page 1

INSTRUCTIONS FOR USE Before use, mix base and hardener components thoroughly. Mixing ratio : 87,0 base : 13,0 hardener (by weight) 80,0 base : 20,0 hardener (by volume) Do not prepare more material than can be applied within the pot life of the mixture. Induction time 10 minutes at temperatures of 15 ºC and lower; none at temperatures above 15 ºC 5 hours at 25 ºC 8 hours at 20 ºC 16 hours at 10 ºC Application with Type thinner % of thinner Nozzle orifice Nozzle pressure Cleaning Brush/roller IJmopox thinner 0-5% n.a. n.a. IJmopox thinner Air spray IJmopox thinner 10 - 15 % 1,5 -2,5 mm 3 - 4...

 Open the catalog to page 2

SAFETY INFORMATION See the corresponding Material Safety Data Sheet for detailed instructions on safety, disposal and health. Date: September ’14 355-99999 Disclaimer Although the information and recommendations are presented in good faith and believed to be correct at date of issue, De IJssel Coatings B.V. makes no representations as of the completeness or accuracy thereof. In no event De IJssel Coatings B.V. will be responsible for damages of any nature whatsoever resulting from the use of this information.

 Open the catalog to page 3

All De IJssel Coatings catalogs and brochures

  1. TWEECOLUX

    3 Pages

  2. Epoxy Gel

    3 Pages

  3. Balsaplast

    2 Pages

  4. KARAAT

    2 Pages

  5. DUBBEL UV

    2 Pages

  6. DOUBLE COAT

    2 Pages