DOUBLE COAT SATIN DESCRIPTION Double Coat Satin is a silk gloss two component finish based on saturated polyester resins and modified aliphatic isocyanate hardeners. PRINCIPAL CHARACTERISTICS Good levelling, easy application by brush, roller of spray; Good resistance to various chemicals; Excellent scratch and mar resistance; Excellent gloss and colour retention; Good adhesion to various materials (even without the use of primers); Suitable as finishing coat in two component paint systems for properly pre-treated wood, steel, aluminium, epoxy, GRP, ABS, etc. COLOURS AND GLOSS Transparent, white or black, other colours on request - High gloss BASIS PROPERTIES (AT Density Solid content Recommended d.f.t. Dust dry after Full cure after Recoating interval 23˚C AND 50% R.H.) : approx. 1,2 g/cm3 (depending on colour) : approx. 52 % (volume) : 35 - 70 µm (dry), depending on application : approx. 2 hours : approx. 5 days, see additional information : min. 24 hours, see additional information max. unlimited, provided gritpapered, clean and dry Shelf life : separate components, stored cool an dry in original packaging, minimum 12 months Flash point (DIN53213) : Double Coat base component 44 oC Double Coat hardener 45 oC SPREADING RATE At 35 µm (d.f.t.) : 12,3 m2/kg (14,8 m2/l) At 50 µm (d.f.t.) : 8,6 m2/kg (10,4 m2/l) At 70 µm (d.f.t.) : 6,2 m2/kg ( 7,4 m2/l) The practical spreading rate depends on a number of variables, such as: shape and size of object to be painted, the condition and profile of the substrate, the method of application, climatologic conditions and skill of labour. SUBSTRATE CONDITION AND TEMPERATURE All substrates : clean and dry, in good condition, free from any contamination and loose particles, pre-treated with IJmopox ZF primer, IJmopox HB coating or Variopox Injection resin and Double Coat high gloss, sanded with grit paper P320. During application and curing a minimum temperature of 15 ºC is allowed. The temperature of the substrate should be minimum 3 ºC above dew point. INSTRUCTIONS FOR USE Before use, mix base and hardener components thoroughly. Mixing ratio : 67,0 base : 33,0 hardener (by weight) The mixing ratio by volume depends on colour. Do not prepare more material than can be applied within the pot life of the mixture.

 Open the catalog to page 1

DOUBLE COAT SATIN Induction time Pot life Application with Type thinner % of thinner Nozzle orifice Nozzle pressure Cleaning 30 minutes at 20 ºC 2 hours at 25 ºC (depending on colour) 3 hours at 20 ºC (depending on colour) 4 hours at 15 ºC (depending on colour) : Brush/roller Brush thinner 3-5% n.a. n.a. Brush thinner Air spray Spray thinner 5 - 15 % 1.2 - 1.4 mm 2 - 3 bar Spray thinner ADDITIONAL INFORMATION Recoating and curing of Double Coat Satin Minimum Maximum, with Double Coat Satin, without sanding Maximum, after sanding with grit paper P320-P400 Fully cured after Application of...

 Open the catalog to page 2

All De IJssel Coatings catalogs and brochures

  1. TWEECOLUX

    3 Pages

  2. Epoxy Gel

    3 Pages

  3. Balsaplast

    2 Pages

  4. KARAAT

    2 Pages

  5. DUBBEL UV

    2 Pages

  6. DOUBLE COAT

    2 Pages